Strength of high-cycle fatigue of non-homogeneous cast iron

Leonavičius, Mindaugas Kazimieras; Bobyliov, Konstantin; Krenevičius, Algimantas; Šukšta, Marijonas; Stupak, Stanislav

Use this URL to cite this publication: https://hdl.handle.net/20.500.14911/141897

Strength of high-cycle fatigue of non-homogeneous cast iron

Details

Publication Type (CRIS)

Straipsnis recenzuojamoje užsienio konferencijos medžiagoje / Article in peer-reviewed foreign conference proceedings (P1g)

Publication Type (eLABa)

Straipsnis recenzuotame konferencijos darbų leidinyje / Article published in peer-reviewed conference proceedings (P1d)

Author(s)

Author	Affiliation
Leonavičius, Mindaugas Kazimieras	Taikomosios mechanikos katedra / Department of Applied Mechanics (0260)
Bobyliov, Konstantin	Taikomosios mechanikos katedra / Department of Applied Mechanics (0260)
Krenevičius, Algimantas	Taikomosios mechanikos katedra / Department of Applied Mechanics (0260)
Šukšta, Marijonas	Taikomosios mechanikos katedra / Department of Applied Mechanics (0260)
Stupak, Stanislav	Taikomosios mechanikos katedra / Department of Applied Mechanics (0260)

Title

Strength of high-cycle fatigue of non-homogeneous cast iron

[en]

M. Leonavičius, K. Bobyliov, A. Krenevičius, M. Šiukšta, S. Stupak

Is part of

EUROMECH - MECAMAT 2006, 9th European Mechanics of Materials Conference, Local approach to fracture: Moret sur Loing, France May 9 - 12, 2006

Published In

Year	Start Page	End Page
2006	335	340

Publisher

Paris : Mines Paris, 2006

Extent

p. 335-340

URI

URI
https://hdl.handle.net/20.500.14911/141897

Cited references

Science / Art Area

Technologijos mokslai / Technological sciences (T)

Field of Science / Art

Mechanikos inžinerija / Mechanical Engineering (T009)

Keywords (en)

Abstract (en)

CT specimens prepared of a special casting which cast technology correspond to an equipment cast technology in such a way that to have structure with a spherical graphite and voids was tested. The threshold AK,f, was give by a well-know method for ^ specimens with voids varies with extent of defects and is lower that without defects. After an evaluation of the decrease of geometric indices because of defects the cracking threshold of non-homogeneous materials is similar to homogenous material.